| Grades |
 |
 |
 |
 |
DIN |
AISI |
UNS |
EN Norm |
Material data sheet |
Density |
 |
|
| 1.4301 | | 1.4301 Material Description and Application | Discription:
austenitic stainless chromium-nickel steel. Has good corrosion resistance, especially in natural environmental media and in the absence of significant chlorine and salt concentrations and welding work.
| Application:
Slightly polluted water and waste water, food, and organic acids, generally resistant to pH 4.5 in low-chloride pleas. It also finds application in the chemical industry, petroleum industry and the petrochemical industry.
| | Miscellaneous: P 0,045;S 0,015 |
|
| | 1.4301 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,08 | 17,0-19,5 | | 8,0-10,5 | 2,0 | | 0,11 | 1,0 |
|
| | 1.4301 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4316 | | 1.4301 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1000 - 1080 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4301 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,80,100 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,80,100 | | 2500 x 6000 | 8,10,12,15,16,18,20,22,25,30,35,40,45,50,55,60,65,70,80 | | 3000 x 6000 | 8,10,12,16,20,30,70 | | 3400 x 6800 | 8,10,12,15 |
|
| X 5 CrNi 18-10 | 304 | S30400 | EN 10028-7 | | 7,90 | | | | 1.4307 | | 1.4307 Material Description and Application | Discription:
austenitic stainless chromium-nickel steel. Has good corrosion resistance, especially in natural environmental media and in the absence of significant chlorine and salt concentrations and welding work.
| Application:
Slightly polluted water and waste water, food, and organic acids, generally resistant to pH 4.5 in low-chloride pleas. It also finds application in the chemical industry, petroleum industry and the petrochemical industry.
| | Miscellaneous: P 0,045; S 0,015 |
|
| | 1.4307 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 17,5-19,7 | | 8,0-10,0 | 2,0 | | 0,11 | 1,0 |
|
| | 1.4307 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4316 | | 1.4307 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1000 - 1080 | Cooling method: | ≤ 2 mm moved air, 2 mm water |
|
| | 1.4307 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,80,100 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,80,100 | | 2500 x 6000 | 8,10,12,15,16,18,20,22,25,30,35,40,45,50,55,60,65,70,80 | | 3000 x 6000 | 8,10,12,16,20,30,70 |
|
| X 5 CrNi 18-9 | 304L | S 30400 | EN 10028-7 | | 7,90 | | | | 1.4362 | | 1.4362 Material Description and Application | Discription:
Ferritic-austenitic, non-corroding steel, alternative material to 1.4571 and 1.4404, with low nickel and molybdenum content and significantly higher proportion of chromium | Application:
Is used in the construction industry, the chemical industry, the petroleum industry, in electronic equipment, in mechanical engineering and in shipbuilding etc., due to its relatively low nickel content compared to conventional austenite economically very attractive
| | Miscellaneous: P 0,035; S 0,015; Cu 0,6 |
|
| | 1.4362 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 24,0 | 0,6 | 5,5 | 2,0 | | 0,2 | 1,0 |
|
| | 1.4362 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4430 | | 1.4362 Heat treatment | | Hot forming: 1150-950 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | 950-1050 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4362 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 8,10,12,15,18,20,25,30,35,40,45,50,55,60 | | 2000 x 6000 | 8,10,12,15,18,20,25,30,35,40,45,50,55,60 | | 2500 x 6000 | 8,10,12,15,18,20,25,30,35,40,45,50,60 |
|
| X2 CrNi 23-4 | | S 32304 | EN 10028-7 | VdTÜV-WB 496 | 7,80 | | | | 1.4404 | | 1.4404 Material Description and Application | Discription:
Austenitic, non-corroding steel displays good acid resistance | Application:
In chemical apparatus construction, sewage plants, paper industry, mainly with high chloride content | | Miscellaneous: |
|
| | 1.4404 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 16,5-18,5 | 2,0-2,5 | 10,0-14,0 | 2,0 | | | 1,0 |
|
| | 1.4404 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4430 | | 1.4404 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1020 - 1100 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4404 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,30,35,40,45,50,60,65,70,80,100 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,30,35,40,45,50,60,65,70,80,100 | | 2500 x 6000 | 6,8,10,12,15,16,20,25,30,35,40,45,50,60,70,80 |
|
| X 2 CrNiMo 17.12.2 | 316L | S 31603 | EN 10028-7 | | 8,00 | | | | 1.4435 | | 1.4435 Material Description and Application | Discription:
Austenitic, non-corroding steel, resistant to organic acids such as lactic, formic, tartaric and acetic acids in high concentrations and at high temperatures | Application:
Higher resistance than V4A to non-oxidizing acids and chloride-containing corrosive agents, is used in the fertiliser industry, the rubber industry, the plastics industry, etc | | Miscellaneous: Cu 0,11; S = 0,015 |
|
| | 1.4435 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 17,0-19,0 | 2,5-3,0 | 12,5-15,0 | 2,0 | | | 1,0 |
|
| | 1.4435 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4430 | | 1.4435 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1020 - 1100 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4435 Delivery programme | | No information was found for this category. |
|
| X 2 CrNiMo 18.14.03 | 316L | S 31603 | EN 10028-7 | | 8,00 | | | | 1.4439 | | 1.4439 Material Description and Application | Discription:
Austenitic, non-corroding steel, excels in numerous acids (sulphuric, phosphoric and organic acids) and in media containing moderate amounts of chloride, known for urea-resistant quality | Application:
In the event of exposure to chloride-containing sulphuric acid and phosphoric acid corrosive agents, used in pipeline and apparatus construction, fertiliser industry, rubber industry etc. | | Miscellaneous: S=0,025 |
|
| | 1.4439 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 16,5-18,5 | 4,0-5,0 | 12,5-14,5 | 2,0 | | 0,12-0,22 | |
|
| | 1.4439 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4440 | | 1.4439 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1040 - 1120 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4439 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 6,8,10,12,15,16,20,25,30,35,40,50 | | 2000 x 6000 | 6,8,10,12,15,16,20,25,30,35,40,50 | | 2500 x 6000 | 6,8,10,12,15,16,20,25,30,35,40,50 | | 3000 x 6000 | 6,8,10,12,15,16,20,25,30,35,40,50 |
|
| X 2 CrNiMoN 17.13.5 | 317LMN | S 31726 | EN 10028-7 | VdTÜV-WB 405 | 8,02 | | | | 1.4462 | | 1.4462 Material Description and Application | Discription:
Ferritic-austenitic, non-corroding steel, good resistance to pitting and intercrystalline corrosion | Application:
stress corrosion cracking in neutral, chloride-containing media, especially with phosphoric and organic acids; resistance under acid gas conditions, used in chemical apparatus construction, in the cellulose and food industries, saltwater pipeline systems | | Miscellaneous: P≤0,035; S≤0,15 |
|
| | 1.4462 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 21,0-23,0 | 2,5-3,5 | 4,5-6,5 | 2,0 | | 0,1-0,11 | 1,0 |
|
| | 1.4462 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: ~1.4462 | | 1.4462 Heat treatment | | Hot forming: 1200-900 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | 1020-1100 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4462 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 3,4,5,6,8,10,12,15,16,20,25,30,35,40,45,55,60,65,70,80 | | 2000 x 6000 | 3,4,5,6,8,10,12,15,16,20,25,30,35,40,45,55,60,65,70,80 | | 2500 x 6000 | 3,4,5,6,8,10,12,15,16,18,20,25,30,35,40,45,50,60,65,70,80 |
|
| X 2 CrNiMoN 22-5-3 | | S 31803 | EN 10028-7 | VdTÜV-WB 418 | 7,80 | | | | 1.4501 | | 1.4501 Material Description and Application | Discription:
Further development of 1.4462 by enrichment with tungsten and/or copper, is characterised by a further increase in resistance to pitting and crevice corrosion and stress corrosion cracking and by an increase in strength parameters
| Application:
Is made into pipes for the gas and oil industry, in shipbuilding and in the chemical industry
| | Miscellaneous: P 0,035; S 0,015;W 0,5 - 1,0; Cu 0,5 - 1,0 |
|
| | 1.4501 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,03 | 24,0 - 26,0 | 3,0 - 4,0 | 6,0 - 8,0 | 1,0 | | 0,20 - 0,30 | 1,0 |
|
| | 1.4501 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: keine | | 1.4501 Heat treatment | | Hot forming: 1150-1000 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | 1040-1120 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4501 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 6,10,12,15,20,25 | | 2000 x 6000 | 6,10,12,15,20,25 | | 2500 x 6000 | 6,10,12,15,20,25 |
|
| X2CrNiMoCuWN 25 7 4 | | S 32760 | EN 10028-7 | | 8,0 | | | | 1.4539 | | 1.4539 Material Description and Application | Discription:
Excellent resistance to pitting, stress corrosion cracking and intercrystalline corrosion | Application:
Applications in seawater technology, offshore, the chemical industry, the paper industry, the cellulose industry | | Miscellaneous: Cu 1,0-2,0; P = 0,03; S = 0,01 |
|
| | 1.4539 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,02 | 19,0-21,0 | 4,0-5,0 | 24,0-26,0 | 2,0 | | 0,15 | 0,70 |
|
| | 1.4539 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: ~1,4539 u. 2.4653 | | 1.4539 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1080 - 1150 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4539 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 3,4,5,6,8,10,12,15,16,18,25,30,35,40,50 | | 2000 x 6000 | 3,4,5,6,8,10,12,15,16,18,25,30,35,40,50 | | 2500 x 6000 | 3,4,5,6,8,10,12,15,16,18,25,30,35,40,50 |
|
| X 1 NiCrMoCuN 25 20 | 904L | N 08904 | EN 10028-7 | VdTÜV-WB 421 | 8,0 | | | | 1.4541 | | 1.4541 Material Description and Application | Discription:
Austenitic, non-corroding steel, good resistance to organic acids such as lactic and acetic acids, good resistance to hydrogen sulphide and intercrystalline corrosion | Application:
Water and slightly polluted effluents, food and organic acids, generally resistant up to pH value 4.5 in low-chloride corrosive agents, use in the chemical industry, film and photography industry, in the building trade, superheater flues in steam power plants
| | Miscellaneous: Cu 2,5-4,0; S 0,015; P 0,045 |
|
| | 1.4541 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,08 | 17,0-19,0 | | 9,0-12,0 | 2,0 | 5 x % C bis 0,7 | 0,05 | |
|
| | 1.4541 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4551 u. 1,4316 | | 1.4541 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1020 - 1100 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4541 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2500 x 6000 | 8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 |
|
| X 6 CrNiTi 18 10 | 321 | S 32100 | EN 10028-7 | | 7,90 | | | | 1.4571 | | 1.4571 Material Description and Application | Discription:
Austenitic, non-corroding steel, good resistance to most acids, even at higher concentrations, temperatures, to intercrystalline corrosion. The addition of titanium prevents the depletion of chromium carbides in the grain boundaries when heated for long periods in the 450-850 °C temperature range
| Application:
Preferred option for use in chemical apparatus construction, sewage plants, paper industry, particularly in the case of high chloride content
| | Miscellaneous: P 0,045; S 0,015 |
|
| | 1.4571 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,08 | 16,5-18,5 | 2,0-2,5 | 10,5-13,5 | 2,0 | 5 x % C bis 0,7 | | 1,00 |
|
| | 1.4571 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4576 u. 1.4430 | | 1.4571 Heat treatment | | Hot forming: 1150 - 750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | *1020 - 1100 | Cooling method: | ≤ 2mm air moved > 2 mm water |
|
| | 1.4571 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2500 x 6000 | 8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 |
|
| X 6 CrNiMoTi 17 12 2 | 316Ti | S 31635 | EN 10028-7 | | 8,00 | | | | 1.4878 | | 1.4878 Material Description and Application | Discription:
Austenitic, non-corroding steel, good resistance to organic acids such as lactic and acetic acids, good resistance to hydrogen sulphide and intercrystalline corrosion | Application:
Water and slightly polluted effluents, food and organic acids, generally resistant up to pH value 4.5 in low-chloride corrosive agents, use in the chemical industry, film and photography industry, in the building trade, superheater flues in steam power plants | | Miscellaneous: Cu 2,5 - 4,0; S 0,015; P 0,045 |
|
| | 1.4878 Chemical composition - guide values in % | | C max. | Cr | Mo | Ni | Mn max | Ti | N | SI max | | 0,08 | 17,0-19,0 | | 9,0-12,0 | 2,0 | 5 x % C bis 0,7 | 0,05 | |
|
| | 1.4878 Welding | | Weldability: | good | Special measures and heat treatment: | none | Filler metals: 1.4551 u. 1.4316 | | 1.4878 Heat treatment | | Hot forming: 1150-750 | Cooling method: air | Stress-relieving temperature °C: | | Softening/
*quenching temperature. °C: | 1020-1100 | Cooling method: | ≤ 2 mm moved air, > 2 mm water |
|
| | 1.4878 Delivery programme | | Dimensions /mm | Thickness /mm | | 1500 x 6000 |
2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2000 x 6000 | 2,3,4,5,6,8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 | | 2500 x 6000 | 8,10,12,15,16,18,20,22,25,28,30,35,40,45,50,55,60,65,70,75,80,90,100,110,125 |
|
| X 6 CrNiTi 18 10 | 321 | S 32100 | EN 10028-7 | | 7,90 | | | | |
|
|
|
|